Kaolin Bleaching by Leaching Using Phosphoric Acid Solutions



Legorreta García, Felipe

2015

Román A. Hernández Hernández, Felipe Legorreta García, Leticia E. Hernández Cruz, Arnoldo Bedolla Jacuinde (2015); Kaolin Bleaching by Leaching Using Phosphoric Acid Solutions, Sociedad Química de México, 59(3), 198-202; ISSN 1870-249X


Abstract


This paper presents a study of kaolin ore bleaching from the municipality of Agua Blanca of Iturbide, Hidalgo, México. This process was carried out using solutions of phosphoric acid as the leaching reagent for the iron dissolution process. It is well known that iron oxide is the major contaminant of clay minerals and silicate used in industry. These contents should be decreased, usually by 0.1%, to achieve a required whiteness index of 90% (ISO) or higher. The whitening improves its economic value, making it possible to use it as a high-quality raw material in industries such as ceramics and paper. For this purpose, we examined the effect of parameters such as the concentration of the eaching reagent (0.10 M, 0.50 M, 1 M, and 3 M), temperatura (298-373 K), and pH level (1, 2 and 3). The experimental results showed that the studied variables have a great influence over the ability to obtain an iron dissolution percentage of more than 98% after 2 hours and 373 K.



Producto de Investigación UAEH




Artículos relacionados

DECOLORACIÓN DE ARCILLAS CAOLINÍFERAS POR LIXIVIACIÓN PARA LA OBTENCIÓN DE CAOLÍN CON ALTO ÍNDICE DE...

Influence of the Synthesis Method on the Microstructure and the Electronic Paramagnetic Resonance in...

Evaluación del tamaño de partícula de manganitas de calcio dopadas con europio, sintetizadas por el ...

SÍNTESIS Y CARACTERIZACIÓN DE CaMnO3 DOPADA CON LANTANO OBTENIDA MEDIANTE EL MÉTODO DE COMBUSTIÓN

EXTRACCIÓN LÍQUIDO-LÍQUIDO DE Zn (II) EN DIFERENTES MEDIOS EMPLEANDO COMO EXTRACTANTE EL LÍQUIDO IÓN...

BENEFICIO DE CAOLÍN PROCEDENTE DEL MUNICIPIO DE AGUA BLANCA POR FLOTACIÓN INVERSA: PRUEBAS PRELIMINA...

ESTUDIO DEL EFECTO DE LA TEMPERATURA DE SISNTESIS EN LA ELABORACIÓN DE MANGANITAS DE CALCIO DOPADAS ...

ESTUDIO COMPARATIVO DEL USO DE ÁCIDO CÍTRICO Y UREA EN LA SÍNTESIS DE MANGANITAS DE CALCIO DOPADAS C...

SÍNTESIS DE NANOCOMPÓSITOS DE ZrO2-NANOTUBOS DE CARBONO-Mo.

BLANQUEO DE ARCILLAS CAOLINÍTICAS COLOR CAFÉ POR DISPERSION Y ASENTAMIENTO