Structure and magnetic properties of GdxY1-xFeO3 obtained by mechanosynthesis



Sánchez De Jesús, Félix

2013

A. M. Bolarín-Miró, F. Sánchez-De Jesús, R. Valenzuela, C.A. Cortés-Escobedo, S. Ammar, Structure and magnetic properties of GdxY1-xFeO3 obtained by mechanosynthesis, Journal of Alloys and Compounds (2013-In press). ISSN: 0925-8388.


Abstract


Solid solutions of yttrium?gadolinium orthoferrites GdxY1?xFeO3 (0 ? x ? 1) were prepared by high-energy ball milling. The aim of this work was to study the influence of the synthesis parameters on the crystal structure and the magnetic behavior of these solid solutions. The precursors, Fe2O3, Y2O3 and Gd2O3, mixed in a stoichiometric ratio to obtain these orthoferrites, were milled for different times (up to 5 h). X-ray diffraction and Rietveld refinement were used to elucidate the phase transformation as a function of the milling time. Results showed the complete formation of orthoferrite with an orthorhombic structure (S.G. Pbnm) without any annealing after 5 h of milling for all of the compositions. The effect of the synthesis process and the x value on the crystal structure and the magnetic properties were also studied. All of the synthesized powders demonstrated weak ferromagnetic behavior. In particular, an increase in the maximum magnetization for all the compositions was found, with a maximum that reached 7.7 emu/g for Gd0.75Y0.25FeO3. For Gd0.5Y0.5FeO3, the magnetization decreases down to 2.1 emu/g. A small contamination of metallic Fe was confirmed through electron spin resonance experiments.



Producto de Investigación




Artículos relacionados

SÍNTESIS Y CARACTERIZACIÓN DE CÁTODOS DE CaxLa1-xMnO3 PARA SU APLICACIÓN EN CCOS

EFECTO DE LA MOLIENDA MECANICA Y LOS TRATAMIENTOS TÉRMICOS EN LA OBTENCIÒN DE COMPUESTOS DE NiO Y Mn...

MECANOSÍNTESIS DE MANGANITAS DE LANTANO: EFECTO DE LA RELACIÓN EN PESO BOLAS:POLVO

Mechanosynthesis and magnetic characterization of nanocrystalline manganese ferrites

OBTENCION DE Co-27Cr-6Mo MEDIANTE ALEADO MECANICO PARA POSIBLES APLICACIONES BIOMÉDICAS

OBTENCION DE Co-27Cr-6Mo MEDIANTE ALEADO MECANICO PARAPOSIBLES APLICACIONES BIOMÉDICAS

Amorphization of Co-base alloy by mechanical alloying

EFECTO DEL POLIETILENGLICOL (PEG) Y LA POLIETILENIMINA (PEI) PARA LA SUSPENSION DE PARTICULAS DE NiO...

EFECTO DE LA MOLIENDA MECANICA Y LOS TRATAMIENTOS TÉRMICOS EN LA OBTENCIÒN DE COMPUESTOS DE NiO Y Mn...

REDUCCIÓN QUÍMICA DE NiO-8YSZ PARA LA OBTENCIÓN DE CERMETS Ni-8YSZ ÚTILES COMO ÁNODOS EN CELDAS DE C...