Mechanosynthesis, crystal structure and magnetic characterization of M-type SrFe12O19



Sánchez De Jesús, Félix

2013

F. Sánchez-De Jesús, A. M. Bolarín-Miró, C.A. Cortés-Escobedo, R. Valenzuela, S. Ammar, Mechanosynthesis, Crystal Structure and Magnetic Characterization of M-type SrFe12O19. Ceramics International (In press-2013). ISSN: 0272-8842.


Abstract


M-type strontium hexaferrite was prepared by mechanosynthesis using high-energy ball milling. The influence of milling parameters, hematite excess and annealing temperature on magnetic properties of SrFe12O19 were investigated. Commercial iron and strontium oxides were used as starting materials. It was found that mechanical milling followed by an annealing treatment at low temperature (700 C) promotes the complete structural transformation to Sr-hexaferrite phase. For samples annealed at temperatures from 700 to 1000 C, saturation magnetization values (Ms) are more sensitive to annealing temperature than coercivity values (Hc). The maximum Ms of 60 emu/g and Hc of 5.2 kOe were obtained in mixtures of powders milled for 5 h and subsequently annealed at 700 C. An increase in the annealing temperature produces negligible changes in magnetic saturation and coercivity. An excess of hematite as a second phase produces a slight decrease in the saturation magnetization but leads to a significant increase in coercive field, reaching 6.6 kOe.



Producto de Investigación




Artículos relacionados

Mechanosynthesis and magnetic characterization of nanocrystalline manganese ferrites

OBTENCION DE Co-27Cr-6Mo MEDIANTE ALEADO MECANICO PARAPOSIBLES APLICACIONES BIOMÉDICAS

CARACTERIZACIÓN DE FERRITA DE MANGANESO OBTENIDA POR MECANOSÍNTESIS.

ESTUDIO COMPARATIVO DEL USO DE ÁCIDO CÍTRICO Y UREA EN LA SÍNTESIS DE MANGANITAS DE CALCIO DOPADAS C...

ESTUDIO COMPARATIVO DEL USO DE ÁCIDO CÍTRICO Y UREA EN LA SÍNTESIS DE MANGANITAS DE CALCIO DOPADAS C...

Amorphization of Co-base alloy by mechanical alloying

MECANOSÍNTESIS DE MANGANITAS DE LANTANO: EFECTO DE LA RELACIÓN EN PESO BOLAS:POLVO

EFECTO DEL POLIETILENGLICOL (PEG) Y LA POLIETILENIMINA (PEI) PARA LA SUSPENSION DE PARTICULAS DE NiO...

EFECTO DE LA MOLIENDA MECANICA Y LOS TRATAMIENTOS TÉRMICOS EN LA OBTENCIÒN DE COMPUESTOS DE NiO Y Mn...

EFECTO DEL POLIETILENGLICOL (PEG) Y LA POLIETILENIMINA (PEI) PARA LA SUSPENSION DE PARTICULAS DE NiO...