Synthesis of Y3Fe5O12 (YIG) assisted by high-energy ball milling



Sánchez De Jesús, Félix

2012

F. Sánchez-De Jesús, C.A. Cortés-Escobedo, R. Valenzuela, S. Ammar, A.M. Bolarín-Miró, (2012). Synthesis of Y3Fe5O12 (YIG) assisted by high-energy ball milling. Ceramics International 38, 5257?5263. doi:10.1016/j.ceramint.2012.03.036.


Abstract


Yttrium iron garnet, Y3Fe5O12 (YIG) powders were synthesized by mechanochemical processing (MCP) from Fe2O3 and Y2O3, followed by an annealing. The aim of this work was to demonstrate that MCP followed by annealing at relative low temperatures can induce the formation of nanostructured YIG. The effect of synthesis process on the final magnetic properties was also studied. The precursors mixed in a stoichiometric ratio to obtain YIG were milled at room temperature in a shaker mixer mill with a ball:powder weight ratio of 10:1. In order to achieve a single-phase of nanostructured YIG a short thermal annealing at temperatures from 700 to 1100oC was done. X-ray diffraction (XRD) and scanning electron microscopy (SEM) were used to characterize the synthesized powders. The milling process promotes the formation of a perovskite phase (orthoferrite YFeO3) independent from the milling time; garnet could only be obtained after an annealing process. The partial formation of the garnet phase was observed in mixtures milled for 5 h. In order to obtain a pure YIG, it is necessary to do a post-treatment of an annealing at temperatures of 900C, around 400 oC lower than those used to prepare the material by solid state reaction. Also, the effect of synthesis method into the magnetic behavior of the garnet was shown.



Producto de Investigación




Artículos relacionados

REDUCCIÓN QUÍMICA DE NiO-8YSZ PARA LA OBTENCIÓN DE CERMETS Ni-8YSZ ÚTILES COMO ÁNODOS EN CELDAS DE C...

Estabilidad térmica de manganitas tipo La1-xCaxMnO3 obtenidas mediante mecanosíntesis

EFECTO DEL POLIETILENGLICOL (PEG) Y LA POLIETILENIMINA (PEI) PARA LA SUSPENSION DE PARTICULAS DE NiO...

ESTUDIO COMPARATIVO DEL USO DE ÁCIDO CÍTRICO Y UREA EN LA SÍNTESIS DE MANGANITAS DE CALCIO DOPADAS C...

EFECTO DE LA MOLIENDA MECANICA Y LOS TRATAMIENTOS TÉRMICOS EN LA OBTENCIÒN DE COMPUESTOS DE NiO Y Mn...

EFECTO DE LA CONTAMINACIÓN POR Fe SOBRE La1-XCaXMnO3 (0

REDUCCIÓN QUÍMICA DE NiO-8YSZ PARA LA OBTENCIÓN DE CERMETS Ni-8YSZ ÚTILES COMO ÁNODOS EN CELDAS DE C...

EFECTO DEL POLIETILENGLICOL (PEG) Y LA POLIETILENIMINA (PEI) PARA LA SUSPENSION DE PARTICULAS DE NiO...

SÍNTESIS DE NiMn2O4 ASISTIDA MEDIANTE MOLIENDA DE ALTA ENERGÍA A PARTIR DE MEZCLAS DE NiO-MnO

CARACTERIZACIÓN DE FERRITA DE MANGANESO OBTENIDA POR MECANOSÍNTESIS