Mecanosíntesis y caracterización de ferrita de manganeso.



Bolarín Miró, Ana María

2011

P. Vera-Serna, F. Sánchez-De Jesús, A.M. Bolarín-Miró, A. Martínez, (2011). Mecanosíntesis y caracterización de ferrita de manganeso. Superficie y Vacío Vacío 24(2), 34-38. ISSN: 1665-3521.


Abstract


Mechanosynthesis process was applied to obtain manganese ferrite with formula MnFe2O4, powder oxides of MnO (99% purity) and Fe2O3 (99% purity) was used as raw materials. The high energy milling was performed under air atmosphere using stainless steel vials and hardness steel balls. X-ray Diffraction, Scanning Electronic Microscopy, Termogravimetric Analysis, Miliohmmeter (four-point resistivity measurement), Light scattering and Magnetometer were used to characterize the synthesis powders. The results shown that the MnFe2O4 was obtained at 12 hours of milling time, the material present saturation magnetic of 48 emu/g and electric conductivity of 0.033 S m-1.



Producto de Investigación




Artículos relacionados

OBTENCION DE Co-27Cr-6Mo MEDIANTE ALEADO MECANICO PARAPOSIBLES APLICACIONES BIOMÉDICAS

OBTENCION DE Co-27Cr-6Mo MEDIANTE ALEADO MECANICO PARAPOSIBLES APLICACIONES BIOMÉDICAS

OBTENCION DE Co-27Cr-6Mo MEDIANTE ALEADO MECANICO PARA POSIBLES APLICACIONES BIOMÉDICAS

EFECTO DE LA MOLIENDA MECANICA Y LOS TRATAMIENTOS TÉRMICOS EN LA OBTENCIÒN DE COMPUESTOS DE NiO Y Mn...

ESTUDIO COMPARATIVO DEL USO DE ÁCIDO CÍTRICO Y UREA EN LA SÍNTESIS DE MANGANITAS DE CALCIO DOPADAS C...

Mechanosynthesis and magnetic characterization of nanocrystalline manganese ferrites

SÍNTESIS Y CARACTERIZACIÓN DE CÁTODOS DE CaxLa1-xMnO3 PARA SU APLICACIÓN EN CCOS

ESTUDIO COMPARATIVO DEL USO DE ÁCIDO CÍTRICO Y UREA EN LA SÍNTESIS DE MANGANITAS DE CALCIO DOPADAS C...

CARACTERIZACIÓN DE FERRITA DE MANGANESO OBTENIDA POR MECANOSÍNTESIS

EFECTO DEL POLIETILENGLICOL (PEG) Y LA POLIETILENIMINA (PEI) PARA LA SUSPENSION DE PARTICULAS DE NiO...