Amorphization of Co-base alloy by mechanical alloying



Bolarín Miró, Ana María

2011

A.M. Bolarín-Miró, F. Sánchez-De Jesús, G. Torres-Villaseñor, C.A. Cortés-Escobedo, J.A. Betancourt-Cantera, Amorphization of Co base alloy by mechanical alloying, Journal of Non-crystalline solids-Elsevier Ed, Elsevier Holanda, ISSN: 0022-3093


Abstract


Structural transformations and the amorphization of cobalt base alloy particles are possible when a powder mixture of Co and CrMo is subjected to the mechanical alloying (MA) process. Elemental powders mixed in adequate weight ratios were used as precursors. The process was carried out at room temperature in a shaker mixer mill using vials and balls of hardened steel as milling media, with a ball:powder weight ratio of 8:1. The characterization of the crystalline structure of milled powders was carried out by means of X-ray diffraction to analyze the phase transformations as a function of milling time. The aim of this work was to demonstrate that MA can induce the amorphization of CoCrMo alloy. The evolution of the phase transformation during milling time is reported. The results showed that it is possible to produce a partial solid solution at room temperature of elemental metallic powders Co70Cr30 and Co90Mo10 by mechanical alloying. Using specific experimental conditions, it is also possible to obtain an amorphous phase in a composition Co60Cr30Mo10; first, Cr and Mo were mechanically prealloyed for 9 h to obtain a Cr80Mo20 solid solution, and Co was then added and milled in over 14 h.



Producto de Investigación




Artículos relacionados

Mechanosynthesis and magnetic characterization of nanocrystalline manganese ferrites

EFECTO DE LA MOLIENDA MECANICA Y LOS TRATAMIENTOS TÉRMICOS EN LA OBTENCIÒN DE COMPUESTOS DE NiO Y Mn...

OBTENCION DE Co-27Cr-6Mo MEDIANTE ALEADO MECANICO PARAPOSIBLES APLICACIONES BIOMÉDICAS

EFECTO DE LA CONTAMINACIÓN POR Fe SOBRE La1-XCaXMnO3 (0

MECANOSÍNTESIS DE MANGANITAS DE LANTANO: EFECTO DE LA RELACIÓN EN PESO BOLAS:POLVO

SÍNTESIS Y CARACTERIZACIÓN DE CÁTODOS DE CaxLa1-xMnO3 PARA SU APLICACIÓN EN CCOS

EFECTO DE LA CONTAMINACIÓN POR Fe SOBRE La1-XCaXMnO3 (0

Estabilidad térmica de manganitas tipo La1-xCaxMnO3 obtenidas mediante mecanosíntesis

ESTUDIO COMPARATIVO DEL USO DE ÁCIDO CÍTRICO Y UREA EN LA SÍNTESIS DE MANGANITAS DE CALCIO DOPADAS C...

ESTUDIO COMPARATIVO DEL USO DE ÁCIDO CÍTRICO Y UREA EN LA SÍNTESIS DE MANGANITAS DE CALCIO DOPADAS C...